作者：CHENG Yujie1REN Qiang1ZHANG Lifeng2
作者單位：1.Yanshan University2. North China University of Technology
會議錄名稱：第九屆國際耐火材料學術會議
出版年：2024-10-15
起頁：195-198
止頁：
總頁數：0
館藏號：
分類號：TQ175.7;TF70
語種：英文
會議名稱：第九屆國際耐火材料學術會議
會議地點：中國四川成都
會議時間：2024-10-15
會議主辦者：中國金屬學會耐火材料學會
關鍵詞：magnesia refractory;high carbon Si Mn-killed;interface;inclusion;
內容簡介In the current study, the reaction between the industrial MgO refractory and the high carbon SiMn-killed steel was investigated using laboratory experiments. The penetration of the molten steel into the MgO refractory was small and the composition of inclusions in the steel changed very little after the reaction of 90 minutes. The penetration of the molten steel into MgO refractory at the interface was hardly detected. A new interface layer containing Al2O3 and MgO with the ...