作者：KOJI MORIWAKI;YOSHIHIRO FUKAI;KOZO KANAMARU;
作者單位：Shinagawa Refractories Co., Ltd
刊名：Journal of the Technical Association of Refractories
ISSN：0285-0028
出版年：2007-01-05
卷：27
期：2
起頁：112
止頁：0
分類號：TQ175
語種：英文
關鍵詞：
內容簡介As a result of the method of evaluating the spalling resistance of SV plates, focusing on crack formation around the nozzle hole, the comparison of damage between samples was simplified by changing the shape of the test samples. Based on the testing of several kinds of samples, the crack formation could not be correlated with the conventional spalling parameter: S alpha E~(-1) centre dot alpha~(-1), whereby it was considered necessary to correlate with other factors concerned.